There are precautions provided in ASTM A/AM that should be considered to prevent embrittlement, as well as selecting steels with appropriate. Practice ASTM A provides guidance on safeguarding against warpage and be stress relieved per the guidelines provided within ASTM A, Section 6. ASTM A / AM Standard Practice for Safeguarding Against Embrittlement of Hot-Dip Galvanized Structural Steel Products and Procedure.

Author: Faule Kazahn
Country: Cuba
Language: English (Spanish)
Genre: Photos
Published (Last): 10 June 2009
Pages: 474
PDF File Size: 5.67 Mb
ePub File Size: 15.43 Mb
ISBN: 112-9-51331-915-2
Downloads: 72814
Price: Free* [*Free Regsitration Required]
Uploader: Shaktihn

Posting Guidelines Promoting, selling, recruiting, coursework and thesis posting is forbidden. It is informational only and not an official part of the standard; the full text of the standard itself must be referred to for its use and application.

ASTM Specifications | American Galvanizer’s Association

Fabrications can have more than one material category, such as a frame assembly. Active view current version of standard. Finally, there are requirements for passivating the material chromating to prevent reaction between concrete and the zinc coating, and on bend diameters.

Any combination of these products can be assembled into a single fabrication and then hot-dip galvanized. This test method deals with the standard procedures for establishing the relative bond strength of steel reinforcing bars in concrete using beam-end specimens.

This practice is applicable to chromate coatings of the colorless both one and two-dipiridescent yellow or bronze, olive drab, black, colorless anodic, yellow or black anodic types, and of the dyed variety, when applied to surfaces of electrodeposited zinc, mechanically deposited zinc, hot-dipped zinc, rolled zinc, electrodeposited cadmium, or mechanically deposited coatings.

Referenced Documents purchase separately The documents listed below are referenced within the subject standard but are not provided as part of the standard. The following is a summary of the various pertinent hot-dip galvanizing specifications. Within the text of this practice and where appropriate, SI units are shown in brackets. Eddy-current-type thickness measurement is a non-destructive test measuring variations in the impedance of a eddy-current inducing coil caused by coating thickness variations.

The specification outlines three acceptable forms of touch-up: The requirements for finish, appearance, and adherence are identical to those in the other main standards. KnowledgeBase What is EN ? Inch-pounds and SI aastm are not necessarily exact equivalents. This specification covers prime western grade-recycled PWG-R zinc made by recycling zinc secondary materials including but not limited to drosses and skimmings.

  FLOOR PLAN MANAGER IN WEB DYNPRO ABAP PDF

This specification covers cold-formed welded and seamless carbon steel round, square, rectangular, or special shape structural tubing for welded, riveted, or bolted construction of bridges and buildings, and for general structural purposes. The LCC analysis considers not only the initial cost of the system but also the future costs maintenance, replacement, etc.

There are coating thickness minimums, but no maximums, and the threads are not subject to the coating thickness requirement.

The Eng-Tips staff will check this out and take appropriate action. If so, how do you handle the testing requirements? After galvanizing, these products should be air cooled instead of quenched to minimize induced stress from the cooling cycle.

However, there are a few additional requirements for galvanized rebar. Practice for Repair of Damaged and Uncoated Areas of HOt-Dip Galvanized Coatings covers appropriate methods used to repair damaged hot-dip galvanized coatings on hardware, structural a13, aatm other hot-dip galvanized products, including uncoated areas remaining after initial hot-dip galvanizing.

If rebar is bent fabricated after the galvanized coating is applied and any flaking or cracking occurs, it zstm not rejectable. See Specifying Duplex Systems for more information. The specification requirements asm coating thickness only contain minimums, there is no maximum coating thickness limitation in the specification.

Open-hearth, basic-oxygen, and electric-furnace steels shall be used for galvanizing. A requires a continuous, smooth, and uniform finish with no uncoated areas including on the threads or issues that interfere with its intended use. Additionally, the installation of diagonal members should be performed after galvanizing.

Students Click Here Join Us! Steel materials and nuts shall be manufactured, processed, and formed as appropriate for their respective grades. Inch-pounds and SI units are not necessarily exact equivalents. Requirements concerning the renovation of qstm areas after initial hot-dip asrm are contained within the material specifications A, A, A Was this answer helpful?

  DIAMOND MORTENSEN PISSARIDES PDF

This test method shall determine the effects of surface preparation or condition such as bar coatings on the bond strength of deformed steel reinforcing bars to concrete. February 14, Authored by Bernardo A.

Astmm requirements of this specification are very similar to those in A, except for the addition of threaded products and embrittlement requirements. Conditions of fabrication may induce a susceptibility to embrittlement in certain steels that can be accelerated by galvanizing.

ASTM Specifications

Conditions of fabrication may induce a susceptibility to embrittlement in certain steels that can be accelerated by galvanizing. A second type asym embrittlement, hydrogen embrittlement, is recognized when stresses are applied to the steel in use. Other materials that can be galvanized include continuous cast slabs, steel or iron castings, and wrought iron.

The following can cause warpage and distortion: Symmetrical sections such as I-beams x143 tubing will be less likely to distort than asymmetrical pieces camber beams, channels, tees, custom beams, girders because the thermal expansion forces above and below the natural axes balance each other.

The purpose of the calculation is to provide justification for the purchase of a higher initial cost system with a low life-cycle cost over an atsm less expensive coating which asym high future costs. Link to Active This link will always route to the current Active version of the standard.

Oftentimes sheet or plate can be returned to a flattened state using a jig or by weighing the product down on a flat surface asym the cool-down. Medias this blog was made to help people to easily download or read PDF files. This tubing shall be produced in both welded and seamless sizes and must have the chemical requirements of carbon, manganese, phosphorus, sulfur, and copper. Embrittlement is not a common occurrence, however, and this discussion does not imply that galvanizing increases embrittlement where good fabricating and galvanizing procedures are employed.

Join your peers on the Internet’s largest technical engineering professional community.